Black Knight Airport Grade Driveway Sealer is designed to be used as a premium coating for the sealing, protecting, preserving and beautifying of old and new driveways, parking lots and other asphalt surfaces such as airport aprons. |
|
|
PRODUCT
DESCRIPTION
Black Knight Airport Grade Sealer is a premium quality asphalt emulsion driveway sealer. |
|
ADVANTAGES
·
Airport technology brought to consumer driveways
·
Three times more durable than
competitive brands
·
Premium protection from stains
and chemical spills
·
Less tracking
·
Quicker drying
|
YOU
NEED
·
Crack Filler
· Pot Hole Filler
· Oil Spot Primer
· Asphalt Cleaner
· Roller or Driveway Brush |
|
PACKAGING
Available
in lithographed 17 Litre Pail.
|
COVERAGE
Maximum coverage 38m sq. (400 Square feet) per 17 litre pail . |
|
WARRANTY
The consumer shall satisfy themselves of the suitability of this product for the intended purpose. Weather, applicator's skill and surface conditions are beyond manufacturer's control. We, therefore, limit our liability to replacement of defective material only, within two years of proof of purchase.
|
|
|
Application
Guide
|
|
STEP
#1: Sweep and clean entire surface. Wash with Black
Knight Asphalt Cleaner or strong detergent and let dry.
STEP #2: Treat oil and chemical stains with Black Knight
Oil Spot Primer.
STEP #3: Remove severely damaged areas and replace with
well compacted Black Knight POT HOLE FILLER. Allow up
to 90 days to harden before applying driveway sealer
STEP #4: Repair cracks with Black Knight Driveway Crack
Filler.
STEP #5: Dampen surface with water and remove puddles
STEP #6: Mix thoroughly
STEP #7: Using a roller or brush, apply a thin even coat of undiluted sealer. Allow to dry a minimum of 24 hours until no longer tacky. Allow a minimum of 3 hours sunlight to cure finish.
STEP #8: If required, apply a second coat crosswise
to first coat. Allow to dry between coats. Apply in
dry weather with temperatures above 10°C (50°F) that will
remain above 10°C (50°F) for more than 24 hours after
application.
|
|
|